脱蜡铸造法有两大类：实心模法和陶壳模法，后者为前者的改良法。 There are two kinds of dewaxing method: solid mold and ceramic shell mold, which is the modified method of the former. 实心模法系在考虑蜡型的冷凝收缩量，铸模的加热膨胀量和熔融金属的冷凝收缩量之后，制作与最 The solid mold is considered to be the most effective in the consideration of the condensation shrinkage of the waxy type, the heating expansion of the mold and the condensing shrinkage of molten metal 终铸件尺寸近似的模具。将融化的蜡质押灌注入此以金属或硅胶做成之模具内，取出蜡型后，浸入微粉 Mould of final casting size. The melted wax will be poured into the mould made of metal or silicone, and then dipped into the powder 耐火材料与粘结剂混泡而成之浆液。 The paste of refractory and binder. 滴净之后，撒布粗粒耐火材料，使之干燥。放入铸框，将混练有粘结剂的耐火物粒填满之，然后干 When the droplets are clean, the fire-resistant material is dried out. Put in the cast frame and fill it with a mixture of refractory grains, and then dry 燥。接着加热使蜡质熔化流出来，作成铸模。以高温加热铸模，烧除少量残余之蜡质并提高其强度，接 Dry. Then the heat melts the wax out and makes a mold. Heat the mold at high temperature, burning the residue wax and improving the strength 着注入金属熔液。 Injection of molten metal. 陶壳模法直到蜡型的制作都跟实心模法相同，只是在一次沾浆和淋砂（或浮砂）之后，并不进行包 The moulding of the ceramic shell is the same as that of the solid mold, but after a paste and drizzle (or floating sand), it is not a bag 模作业，而是反复多次地进行沾浆和淋砂，直至获得预定的外壳厚度。干燥、加热、熔流出蜡质，高温 The die is done, but it is repeated and repeated over and over again until the desired thickness of the shell is obtained. Drying, heating, molten wax, high temperature 加热再行浇注，这种方法为目前的脱蜡精密铸造业者所广泛采用。 This method is widely adopted by the current dewaxing precision foundry.